SUBMERGED ARC WELDING WIRE: SW-EH14
Specification：AWS A5.17 EH14
ASME/SFA 5.17 EH14
ISO 14171-A S4
ISO 14171-B: SU41
CSA W48 F49A4-EH14-H8
JIS Z 3351 YS-S4/S6
GB/T 5293 SU41
Introduction：
Submerged wire for 490Mpa grade high tensile carbon steel .
Low S and P content minimizes weld sensitivity to hot cracking and ensures high low-temperature impact toughness.
Kind of high-manganese type welding wire, matches with low-manganese and low-silicon type welding flux, eg: sintered flux SJ101.
Well weldability: stable arc, easy slag removal,neat weld bead.
Application：
Wind turbine tower
Steel structure
Bridges
Ships
Pressure Vessel
Pipeline
Pass the certification：
CE、ABS、JIS、DNV、CWB、LR、GL、CCS
Chemical Composition of Wire %：
| C | Mn | Si | P | S | Ni | Cr | Mo | |
| AWS | 0.10-0.15 | 1.75-2.20 | ≤0.10 | ≤0.025 | ≤0.025 | ≤0.15 | ≤0.15 | ≤0.15 |
| TR(HC) | 0.13 | 1.96 | 0.05 | 0.014 | 0.004 | 0.01 | 0.03 | 0.02 |
Mechanical Properties of Deposited Metal：
| Tensile Strength | Yield Strength | Elongation | Impact Value | |||||
| Mpa | Mpa | % | -20℃ J | |||||
| TR(HC) | 580 | 475 | 30 | 115 | ||||
Diameter/Packing：
| Diameter | Hollow Coil | Drum | Spool | Basket | |||||||
| mm/in | 25kg(55lbs) | 50kg(110lbs) | 60Kg(132lbs) | 100Kg(220lbs) | 150Kg(330lbs) | 250Kg(550lbs) | 350Kg(770lbs) | 250Kg(550lbs) | 350Kg(770lbs) | 20Kg(44lbs) | 25kg(55lbs) |
| 1.0(0.040) | √ | √ | |||||||||
| 1.2(0.045) | √ | √ | |||||||||
| 1.4(0.052) | √ | √ | |||||||||
| 1.6(1/16) | √ | √ | √ | √ | √ | √ | |||||
| 2.0(5/64) | √ | √ | √ | ||||||||
| 2.4(3/32) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 3.0(0.118) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 3.2(1/8) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 4.0(5/32) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 4.8(3/16) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 5.0(0.197) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 6.0(15/64) | √ | √ | √ | √ | |||||||
| 6.4(1/14) | √ | √ | √ | √ | |||||||
Welding position：PA
Points for Attention：
1. The flux must be baked in a temperature of 300℃~350℃ for 1-2 hours.
2. Remove the oil, dust and rust from the welding parts