SW-EH12K
Hits：56
EH12K
SUBMERGED ARC WELDING WIRE: SW-EH12K
Specification：AWS A5.17 EH12K
ASME/SFA 5.17 EH12K
ISO 14171-B: SUZ42
JIS Z 3351 YS-S5
GB/T 5293 SUZ42
Introduction：
Submerged wire for 490Mpa grade high tensile carbon steel .
Low S and P content minimizes weld sensitivity to hot cracking and ensures high low-temperature impact toughness.
Well weldability: stable arc, easy slag removal,neat weld bead.
Application：
Windpower Generation
Offshore engineering
Bridges
Pressure Vessel
Pipeline
Pass the certification：
Contact us
Chemical Composition of Wire %：
| C | Mn | Si | P | S | Cu | |
| AWS | 0.06-0.15 | 1.5-2.0 | 0.20-0.65 | ≤0.025 | ≤0.025 | ≤0.35 |
| TR(HC) | 0.07 | 1.7 | 0.46 | 0.010 | 0.005 | 0.11 |
Mechanical Properties of Deposited Metal：
| Tensile Strength | Yield Strength | Elongation | Impact Value | |||||
| Mpa | Mpa | % | -20℃ J | |||||
| TR(HC) | 590 | 450 | 26 | 85 | ||||
Diameter/Packing：
| Diameter | Hollow Coil | Drum | Spool | Basket | |||||||
| mm/in | 25kg(55lbs) | 50kg(110lbs) | 60Kg(132lbs) | 100Kg(220lbs) | 150Kg(330lbs) | 250Kg(550lbs) | 350Kg(770lbs) | 250Kg(550lbs) | 350Kg(770lbs) | 20Kg(44lbs) | 25kg(55lbs) |
| 1.0(0.040) | √ | √ | |||||||||
| 1.2(0.045) | √ | √ | |||||||||
| 1.4(0.052) | √ | √ | |||||||||
| 1.6(1/16) | √ | √ | √ | √ | √ | √ | |||||
| 2.0(5/64) | √ | √ | √ | ||||||||
| 2.4(3/32) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 3.0(0.118) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 3.2(1/8) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 4.0(5/32) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 4.8(3/16) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 5.0(0.197) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 6.0(15/64) | √ | √ | √ | √ | |||||||
| 6.4(1/14) | √ | √ | √ | √ | |||||||
Welding position：PA
Points for Attention：
1. The flux must be baked in a temperature of 300℃~350℃ for 1-2 hours.
2. Remove the oil, dust and rust from the welding parts