SW-EA3
Hits：71
EA3
SUBMERGED ARC WELDING WIRE: SW-EA3
Specification：AWS A5.23 EA3
ASME/SFA-5.23 EA3
ISO 14171-A-S3MO
ISO 14171-B SU4M3
JIS Z 3351 YS-M5
GB/T 5293 SUM31
Introduction：
-
For 600Mpa-750Mpa grade low alloy steels, eg: material 18Mo,12MnV,15Mnv.
-
Well weldability: stable arc, easy slag removal,neat weld bead.
Application：
-
Ships
-
Construction machinery
-
Chemistry Industry
-
Bridges
-
Steel Structure
-
Boilers
-
pressure vessels
Pass the certification：
JIS
Chemical Composition of Wire %：
| C | Mn | Si | P | S | Ni | Cr | Mo | Cu | |
| AWS | 0.07-0.15 | 1.30-1.75 | 0.05-0.20 | ≤0.025 | ≤0.025 | ≤0.15 | ≤0.15 | 0.45-0.65 | ≤0.20 |
| TR(HC) | 0.07 | 1.68 | 0.17 | 0.013 | 0.005 | 0.01 | 0.02 | 0.55 | 0.08 |
Mechanical Properties of Deposited Metal：
| Tensile Strength | Yield Strength | Elongation | Impact Value | |||||
| Mpa | Mpa | % | -20℃ J | |||||
| TR(HC) | 680 | 580 | 26 | 85 | ||||
Diameter/Packing：
| Diameter | Hollow Coil | Drum | Spool | Basket | |||||||
| mm/in | 25kg(55lbs) | 50kg(110lbs) | 60Kg(132lbs) | 100Kg(220lbs) | 150Kg(330lbs) | 250Kg(550lbs) | 350Kg(770lbs) | 250Kg(550lbs) | 350Kg(770lbs) | 20Kg(44lbs) | 25kg(55lbs) |
| 1.0(0.040) | √ | √ | |||||||||
| 1.2(0.045) | √ | √ | |||||||||
| 1.4(0.052) | √ | √ | |||||||||
| 1.6(1/16) | √ | √ | √ | √ | √ | √ | |||||
| 2.0(5/64) | √ | √ | √ | ||||||||
| 2.4(3/32) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 3.0(0.118) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 3.2(1/8) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 4.0(5/32) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 4.8(3/16) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 5.0(0.197) | √ | √ | √ | √ | √ | √ | √ | √ | |||
| 6.0(15/64) | √ | √ | √ | √ | |||||||
| 6.4(1/14) | √ | √ | √ | √ | |||||||
Welding position：PA
-
Points for Attention：
1. The Welding flux must be baked under 300-350℃ for 1~2 hours.
2. Remove the oil, dust and rust from the welding parts